Leakage and fire damage caused due to stress corrosion cracking of a heat exchanger at a glycerin concentration plant
|
 |
Knowledge Comment: |
 |
The crack may not be found until the leakage occurred. Thoroughness of obsevation at manufacturing a equipment or piping is important. |
|
|
|
|